Eu/Tb codoped aluminoborosilicate glasses were fabricated by high temperature melting-quenched technique and their luminescence properties were investigated by excitation and emission spectra. Under 376 nm excitation, blue, green and red emission bands were simultaneously observed at 425 nm, 485 nm, 540 nm and 611 nm, respectively. The broad blue emission band centered at 425 nm was originated from the reduced Eu2+ ions, which were reduced from Eu3+ ions at high temperature in an ambient atmosphere and the reduction process may be related with the optical basicity of glass matrix. A complex bright white light emission was obtained for 0.5 mol Eu2O3, 0.5 mol Tb2O3 codoped aluminoborosilicate glass with CIE-X=0.31 and CIE-Y=0.33. The energy transfer among Eu3+, Eu2+ and Tb3+ ions was also discussed.

说明.txt

• We are an exchange download platform that only provides communication channels. The downloaded content comes from the internet. Except for download issues, please Google on your own.
• The downloaded content is provided for members to upload. If it unintentionally infringes on your copyright, please contact us.
• Please use Winrar for decompression tools
• If download fail, Try it againg or Feedback to us.
• If downloaded content did not match the introduction, Feedback to us，Confirm and will be refund.
• Before downloading, you can inquire through the uploaded person information

Nothing．